Pirita (FeS2) 2-THETA INTENSITY D-SPACING H K L 28.57 39.18 3.1276 1 1 1 33.10 95.52 2.7086 2 0 0 37.13 54.86 2.4226 2 1 0 40.82 45.47 2.2115 2 1 1 47.48 51.01 1.9152 2 2 0 56.33 100.00 1.6333 3 1 1 59.07 15.84 1.5638 2 2 2 61.74 16.11 1.5024 3 0 2 64.34 15.90 1.4478 3 2 1 64.34 5.65 1.4478 3 1 2 Calcita CaCO3 2-THETA INTENSITY D-SPACING H K L 23.09 8.36 3.8526 0 1 2 29.44 100.00 3.0337 1 0 4 31.48 2.07 2.8416 0 0 6 36.02 14.36 2.4934 1 1 0 39.46 18.81 2.2834 1 1 3 43.22 14.64 2.0933 2 0 2 47.18 6.50 1.9263 0 2 4 47.58 19.73 1.9112 0 1 8 48.58 20.46 1.8742 1 1 6 56.65 3.42 1.6249 2 1 1 57.48 9.78 1.6032 1 2 2 60.76 5.68 1.5244 2 1 4 61.09 2.63 1.5169 2 0 8 61.47 2.79 1.5084 1 1 9 63.15 2.06 1.4723 1 2 5 64.76 6.70 1.4396 3 0 0 65.72 3.76 1.4208 0 0 12 69.30 1.33 1.3560 2 1 7 70.36 2.30 1.3381 0 2 10 Almandino Fe2+3Al2(SiO4)3 2-THETA INTENSITY D-SPACING H K L 18.84 1.18 4.7107 2 1 1 31.00 37.89 2.8847 4 0 0 34.77 100.00 2.5802 4 2 0 36.52 7.72 2.4601 3 3 2 38.21 20.89 2.3554 4 2 2 39.84 13.17 2.2630 4 3 1 42.93 14.94 2.1067 5 2 1 44.41 3.34 2.0398 4 4 0 48.64 9.61 1.8719 5 3 2 48.64 10.97 1.8719 6 1 1 49.99 1.19 1.8245 6 2 0 55.15 15.42 1.6655 4 4 4 57.60 32.53 1.6002 6 4 0 58.81 1.45 1.5702 5 5 2 60.00 42.44 1.5420 6 4 2 64.62 10.22 1.4424 8 0 0 65.74 1.44 1.4203 7 4 1 Espinelo (MgAl2O4) 2-THETA INTENSITY D-SPACING H K L 18.95 28.48 4.6714 1 1 1 31.21 33.56 2.8606 2 2 0 36.78 100.00 2.4396 3 1 1 38.48 1.51 2.3357 2 2 2 44.73 55.12 2.0228 4 0 0 55.57 9.96 1.6516 4 2 2 59.26 3.28 1.5571 3 3 3 59.26 41.81 1.5571 5 1 1 65.13 71.72 1.4303 4 4 0 68.52 2.31 1.3676 5 3 1 74.01 3.33 1.2793 6 2 0 77.22 9.91 1.2339 5 3 3 82.50 6.13 1.1679 4 4 4 85.63 2.14 1.1330 5 5 1 85.63 2.14 1.1330 5 5 1 Yeso Ca(SO4)·2H2O 2-THETA INTENSITY D-SPACING H K L 11.66 88.21 7.6050 0 2 0 16.53 26.11 5.3683 0 1 1 20.76 100.00 4.2821 -1 2 1 23.41 15.37 3.8025 0 4 0 23.43 12.01 3.7992 0 3 1 29.14 73.30 3.0656 -1 4 1 31.13 52.99 2.8733 1 2 1 33.34 2.57 2.6876 0 5 1 33.39 36.27 2.6842 0 2 2 34.63 2.29 2.5908 -2 0 2 36.00 12.46 2.4949 2 0 0 36.31 23.16 2.4743 -2 3 1 36.65 7.16 2.4524 -2 2 2 37.41 4.35 2.4043 1 4 1 43.37 17.65 2.0860 2 4 0 43.49 4.95 2.0808 -1 2 3 46.47 5.80 1.9539 2 1 1 46.96 3.17 1.9347 1 3 2 47.52 4.73 1.9133 -2 3 3 47.88 17.29 1.8996 0 6 2 48.40 13.69 1.8803 -1 4 3 50.35 15.27 1.8119 -2 6 2 50.76 5.69 1.7982 -3 2 1 50.55 6.42 1.8051 -1 7 2 51.17 2.87 1.7849 -1 8 1 51.37 10.60 1.7782 2 6 0 54.46 2.83 1.6843 -3 2 3 55.18 7.09 1.6641 -3 4 1 55.86 3.96 1.6456 -1 6 3 56.76 6.66 1.6215 -2 0 4 56.77 2.35 1.6212 1 8 1 64.74 4.75 1.4395 1 4 3 64.99 2.44 1.4344 0 0 4 68.70 6.07 1.3658 1 10 1 Topacio Al2SiO4F2 2-THETA INTENSITY D-SPACING H K L 20.21 3.97 4.3989 0 2 0 21.64 8.83 4.1111 1 1 0 22.84 4.70 3.8960 0 2 1 24.12 74.81 3.6918 1 1 1 27.93 86.00 3.1956 1 2 0 29.43 39.61 3.0360 0 2 2 29.93 20.63 2.9863 1 2 1 30.45 100.00 2.9363 1 1 2 36.22 23.22 2.4805 1 3 0 37.53 8.23 2.3968 1 0 3 37.83 17.27 2.3787 1 3 1 38.13 49.10 2.3603 0 2 3 38.95 8.01 2.3125 1 1 3 40.12 3.41 2.2478 2 1 0 41.04 9.67 2.1994 0 4 0 41.60 13.25 2.1713 2 1 1 42.49 4.53 2.1276 0 4 1 42.97 55.18 2.1047 1 2 3 44.05 29.23 2.0555 2 2 0 48.73 24.63 1.8685 1 1 4 49.08 26.62 1.8558 1 3 3 50.06 11.69 1.8219 2 3 0 50.81 6.43 1.7967 1 4 2 51.31 5.51 1.7804 2 3 1 54.93 32.96 1.6711 2 3 2 55.46 8.28 1.6563 2 2 3 56.80 13.77 1.6205 1 4 3 57.68 2.40 1.5978 2 4 0 60.34 10.64 1.5336 2 1 4 60.64 20.14 1.5266 2 3 3 61.02 4.24 1.5180 0 4 4 65.82 38.22 1.4184 1 5 3 66.64 24.37 1.4030 2 5 0 66.88 23.76 1.3985 0 0 6 69.28 37.57 1.3557 3 0 3 Galena PbS 2-THETA INTENSITY D-SPACING H K L 26.04 97.96 3.4279 1 1 1 30.15 100.00 2.9686 2 0 0 43.12 69.58 2.0991 2 2 0 51.04 43.15 1.7902 3 1 1 53.48 22.84 1.7139 2 2 2 62.59 9.90 1.4843 4 0 0 68.94 15.15 1.3621 3 3 1 71.00 25.40 1.3276 4 2 0 Esfalerita ZnS 2-THETA INTENSITY D-SPACING H K L 28.57 100.00 3.1243 1 1 1 33.11 11.98 2.7057 2 0 0 47.52 56.75 1.9133 2 2 0 56.39 36.91 1.6316 3 1 1 59.14 2.94 1.5622 2 2 2 69.48 7.63 1.3529 4 0 0 Cuarzo SiO2 2-THETA INTENSITY D-SPACING H K L 20.88 19.89 4.2548 1 0 0 26.66 69.97 3.3432 0 1 1 26.66 30.03 3.3432 1 0 1 36.58 7.22 2.4565 1 1 0 39.50 1.03 2.2812 0 1 2 39.50 6.26 2.2812 1 0 2 40.33 3.23 2.2364 1 1 1 42.49 5.32 2.1274 2 0 0 45.84 2.10 1.9796 2 0 1 50.19 12.64 1.8178 1 1 2 54.93 3.10 1.6716 0 2 2 55.38 1.64 1.6590 0 1 3 60.02 4.18 1.5414 2 1 1 60.02 5.03 1.5414 1 2 1 64.10 1.75 1.4528 1 1 3 67.81 1.41 1.3820 2 1 2 67.81 4.28 1.3820 1 2 2 68.21 1.38 1.3749 0 2 3 68.21 5.41 1.3749 2 0 3 68.38 4.23 1.3718 0 3 1 Sillimanita Al2SiO5 2-THETA INTENSITY D-SPACING H K L 16.57 18.42 5.3589 1 1 0 23.80 7.29 3.7432 2 0 0 26.12 80.51 3.4148 1 2 0 26.52 100.00 3.3644 2 1 0 30.43 1.05 2.9390 1 2 1 31.01 17.11 2.8860 0 0 2 33.46 26.03 2.6795 2 2 0 35.34 48.45 2.5410 1 1 2 37.16 12.07 2.4207 1 3 0 39.44 9.37 2.2856 2 0 2 40.95 65.27 2.2042 1 2 2 42.83 13.79 2.1120 2 3 0 43.26 3.05 2.0920 3 2 0 48.65 8.38 1.8716 4 0 0 49.74 7.30 1.8330 3 1 2 50.17 1.33 1.8183 4 1 0 51.14 2.96 1.7863 3 3 0 53.68 8.14 1.7074 2 4 0 54.15 6.99 1.6938 3 2 2 54.55 13.21 1.6822 4 2 0 57.69 16.52 1.5977 0 4 2 58.80 8.31 1.5703 4 0 2 59.12 2.67 1.5626 1 4 2 60.14 1.56 1.5384 4 1 2 60.99 38.86 1.5189 3 3 2 64.06 4.23 1.4533 4 2 2 64.57 16.52 1.4430 0 0 4 65.74 3.72 1.4201 2 5 0 67.09 5.81 1.3949 5 2 0 70.24 3.97 1.3397 4 4 0